MELTING POINT( ℃ ) |
DENSITY(g/cm3) |
VISCOSITY(mpa.s 140°C) |
PACKAGING ( KG ) |
HOW TO USE |
110 |
0.95-0.97 |
9-25 |
25(COMPOUND BAG) |
IT CAN BE ADDED IN ANY STEPS. THEN IT SHOULD BE DISPERSED HOMOGENEOUSLY. |
IT IS FISCHER TROPSCH WAX WITH GOOD LEVELLING ABILITY AND SCRATCH RESISTANCE. IT WILL NOT PRODUCE THE SMOKE. IT IS HIGHLY RECOMMENDED IN THE APPLICATION OF POWDER COATINGS.
THE RECOMMENDED ADDITION AMOUNT IS 0.5-1.5% OF THE TOTAL QUANTITY OF THE FORMULA. YOU CAN CHOOSE THE OPTIMUM AMOUNT ACCORDING TO DIFFERENT PRACTICAL NEEDS.
MELTING POINT( ℃ ) |
PENETRATION DEGREE(10-1mm) |
AVERAGE PARTICLE SIZE(μm) |
PACKAGING ( KG ) |
HOW TO USE |
120 |
<1.0 |
4-6 |
20(COMPOUND BAG) |
IT CAN BE ADDED IN ANY STEPS. THEN IT SHOULD BE DISPERSED HOMOGENEOUSLY. |
IT IS A KIND OF MICRONIZED FISCHER TROPSCH WAX WITH EVENLY DISTRIBUTED MOLEULAR WEIGHT. IT HAS LITTLE EFFECT ON THE GLOSS AND GOOD DISPERSIBILITY. IT IS RECOMMENDED IN THE APPLICATION OF INDUSTRIAL PAINT, WAX FOR POWDER COATINGS AND OFFSET PRINTING INK. IT IS VERY COST-EFFECTIVE.
THE RECOMMENDED ADDITION AMOUNT IS 0.5~1.0% OF THE TOTAL QUANTITY OF THE FORMULA. PLEASE CHOOSE THE OPTIMUM AMOUNT ACCORDING TO DIFFERENT PRACTICAL NEEDS.
FREEZING POINT °C |
CONTENT % |
IODINE VALUE |
PACKAGING ( KG ) |
60.0-70.0 |
≥90% |
gI2/100g≦4.0 |
25(COMPOUND BAG) |
IT IS A KIND OF NON-TOXIC PLASTICIZER, ANTI-AGING AGENT AND FOAMING AGENT WIDELY USED FOR THE MANUFACTURE OF POWDER CATINGS. IT EFFECTIVELY IMPROVES THE FLEXIBILITY, PLASTICITY AND ANTISTATIC PROPERTY OF THE PRODUCT.
IT IS A KIND OF WHITE POWDER SUBSTANTIALLY FREE OF IMPURITIES.IT IS INSOLUBLE IN WATER AND SOLUBLE IN ALCOHOL, BENZENE AND ACETONE. IT WILL BE EMULSIFIED TO SOLID WATER-BORNE POLYMER DISPERSION WHEN SHAKED INTENSELY WITH HOT WATER. HLB VALUE OF THE ONE WITH 90% MONOSTEARIN IS 3.9-5.3. IT IS A KIND OF MULTIPURPOSE EMULSIFIER WHICH IS A SAFE INTERNATIONALLY RECOGNIZED FOOD ADDITIVE WITHOUT LIMITED APPLICATION AMOUNT IN FDA.
GLASS TRANSITION TEMPERATURE °C |
ACID VALUE(mg/gKOH) |
APPEARANCE |
PACKAGING ( KG ) |
125 |
285 |
PARTICLE MATTER OR POWDER |
25 |
IT IS A REACTION TYPE OF MATTING AGENT FOR POWDER COATINGS. IT IS APPLICABLE TO THE TRANSPARENT AND MATTE POWDER COATINGS.
IT IS MATTE BLACK WITHOUT BLEACHING. IT HAS GOOD SCRATCH RESISTANCE.
MELTING POINT( ℃ ) |
ACID VALUE(mg/gKOH) |
AMINE VALUE(mg/gKOH) |
PACKAGING ( KG ) |
141.5-146.5 |
≤7.5 |
≤2.5 |
25 |
IT IS APPLIED IN DEFOAMING PROGRESS WHEN USING THE POWDER COATINGS, CAST IRON AND ALUMINIUM MATERIAL.
ADDITION AMOUNT VARIES ACCORDING TO THE QUANTITY OF PIGMENT FILLERS. ADDITION QUANTITY OF THE DEFOAMER: 0.5~5% OF THE FILLER QUANTITY.
PRODUCT CATEGORY |
MELTING POINT( ℃ ) |
ACID VALUE(mg/gKOH) |
APPERANCE |
PACKAGING ( KG ) |
ANTIOXIDANTS |
160-180°C |
≤1.0 |
POWDER WITH SLIGHT ODOR |
25 |
IT IS USUALLY NOT USED SEPARATELY. IT IS WIDELY USED IN THE APPLICATIONS OF MACROMOLECULAR MATERIALS SUCH AS PE, PP, PS, POLYAMIDE, POLYCARBONATE AND ABS AFTER MIXING WITH PHENOLIC ANTIOXIDANTS.
IT IS A KIND OF ORGANIC PHOSPHITE ESTER WITH HIGH PERFORMANCE. IT HELPS TO PREVENT DISCOLORATION OF POLYMERS. DEGRADATION RATE OF THE POLYMERS CAN BE LOWERED. THE PERFORMANCE OF GAS FADING RESISTANCE OF RESIN CAN BE IMPROVED.
PRODUCT CATEGORY |
MELTING POINT( ℃ ) |
PARTICLE SIZE (μm) |
APPERANCE |
PACKAGING ( KG ) |
ANTI-SCRATCH AGENTS |
320°C |
D50:4,D99:10 |
WHITE POWDER |
25 |
IT MAKES THE ALUMINIUM-FOIL PAPER EASY TO BE SHREDDED.
IT IS PURE PTFE WAX, WHICH CAN SIGNIFICANTLY IMPROVE THE ANTI-SCRATCH PROPERTY, ABRASION RESISTANCE AND SMOOTHNESS OF THE COAT.