TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
GENERAL DISPERSING AGENT FOR WATER-BASED TOPCOAT |
40 |
BLOCK COPOLYMER SOLUTION |
WATER |
ACID VALUE: 12(mg/gKOH) |
DENSITY: 1.066g/cm |
THE PRODUCT IS CHARACTERIZED BY HIGH WATER RESISTANCE AND SALT SPRAY RESISITANCE.
IT IS GOOD FOR COGRINDING THE ORGANIC AND INORGANIC PIGMENTS.
ORGANIC AND INORGANIC PIGMENTS, CARBON BLACK, TIO2, ALL KINDS OF FILLER AND METALLIC PIGMENTS CAN BE DISPERSED WITH IT.
IT HAS GREAT UNIVERSALITY WITHOUT FLOATING AND FLOODING. IT IS BETTER FOR SERIES OF INDUSTRIAL PAINTS WITH HIGH CONTENT OF ORGANIC PIGMENTS.
TIO2 8%-10%
INORGANIC PIGMENTS 12%-25%
ORGANIC PIGMENTS 25%-70%
CARBON BLACK 80%-130%
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
GENERAL DISPERSING AGENT FOR WATER-BASED TOPCOAT |
40 |
BLOCK COPOLYMER SOLUTION |
WATER/DPM |
ACID VALUE: 12(mg/gKOH) |
ALKALI EXCLUDED |
THE PRODUCT IS CHARACTERIZED BY HIGH WATER RESISTANCE AND SALT SPRAY RESISITANCE.
IT IS GOOD FOR COGRINDING THE ORGANIC AND INORGANIC PIGMENTS.
ORGANIC AND INORGANIC PIGMENTS, CARBON BLACK, TIO2, ALL KINDS OF FILLER AND METALLIC PIGMENTS CAN BE DISPERSED WITH IT.
IT HAS GREAT UNIVERSALITY WITHOUT FLOATING AND FLOODING. IT IS BETTER FOR SERIES OF INDUSTRIAL PAINTS WITH HIGH CONTENT OF INORGANIC PIGMENTS.
TIO2 8%-10%
INORGANIC PIGMENTS 12%-25%
ORGANIC PIGMENTS 25%-70%
CARBON BLACK 80%-130%
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
GENERAL DISPERSING AGENT FOR WATER-BASED TOPCOAT |
45 |
BLOCK COPOLYMER SOLUTION |
WATER |
ACID VALUE: 15(mg/gKOH) |
GOOD UNIFORMITY |
THE PRODUCT IS CHARACTERIZED BY HIGH WATER RESISTANCE AND SALT SPRAY RESISITANCE.
IT IS GOOD FOR COGRINDING THE ORGANIC AND INORGANIC PIGMENTS.
ORGANIC AND INORGANIC PIGMENTS, CARBON BLACK, TIO2, ALL KINDS OF FILLER AND METALLIC PIGMENTS CAN BE DISPERSED WITH IT.
IT HAS GREAT UNIVERSALITY WITHOUT FLOATING AND FLOODING.
IT HAS GOOD BLENDING PROPERTY, HIGH DISPERSIBILITY AND GOOD VISCOSITY STABILITY.
TIO2 8%-10%
INORGANIC PIGMENTS 12%-25%
ORGANIC PIGMENTS 25%-70%
CARBON BLACK 80%-130%
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
GENERAL DISPERSING AGENT FOR WATER-BASED TOPCOAT |
50 |
BLOCK COPOLYMER SOLUTION |
WATER |
ACID VALUE: 12(mg/gKOH) |
HEAT RESISTANT |
THE PRODUCT IS CHARACTERIZED BY HIGH WATER RESISTANCE AND SALT SPRAY RESISITANCE.
IT IS GOOD FOR COGRINDING THE ORGANIC AND INORGANIC PIGMENTS.
ORGANIC AND INORGANIC PIGMENTS, CARBON BLACK, TIO2, ALL KINDS OF FILLER AND METALLIC PIGMENTS CAN BE DISPERSED WITH IT.
IT HAS GREAT UNIVERSALITY WITHOUT FLOATING AND FLOODING.
IT HAS GOOD WATER SOLUBILITY, GOOD PERFORMANCE OF VISCOSITY REDUCTION AND GOOD VISCOSITY STABILITY IN HIGH TEMPERATURE.
TIO2 8%-10%
INORGANIC PIGMENTS 12%-25%
ORGANIC PIGMENTS 25%-70%
CARBON BLACK 80%-130%
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
GENERAL DISPERSING AGENT FOR WATER-BASED ANTICORROSIVE COATINGS |
60 |
MIXTURE OF POLYURETHANE |
DPM/DBE |
ACID VALUE: 23(mg/gKOH) |
VISCOSITY: 1200CPS |
THE PRODUCT IS VERY APPLICABLE TO ANTICORROSIVE COATINGS BECAUSE IT IS NON-IONIC PIGMENT STABILIZER WITH GOOD CHEMICAL RESISTANCE AND WITHOUT INORGANIC BASE AND APEO.
IT IS SUTABLE FOR DISPERSING ZINC POWDER, INORGANIC PIGMENTS AND ORGANIC PIGMENTS BECAUSE IT IS STABLE IN EPOXY SYSTEM.
IT GENERALLY USED IN PRIMER AND INTERMEDIATE PAINT WITH
HIGH SALT SPRAY RESISITANCE AND LOW VISCOSITY IN HIGH TEMPERATURE.
INORGANIC PIGMENTS 3%-10%
ORGANIC PIGMENTS 15%-50%
ZINC POWDER 2%-5%
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
WETTING AGENT FOR PIGMENTS |
100 |
POLYETHER -MODIFIED ACETYLENIC DIOLS |
NONE |
CLOUD POINT: |
NONIONIC SURFACTANT |
THE PRODUCT IS APPLICABLE TO WETTING THE INDUSTRIAL PIGMENTS WITH GOOD WETTABILITY AND LESS FOAM.
SURFACE TENSION ESPECIALLY THE DYNAMIC SURFACE TENSION IN THE COATINGS SYSTEM CAN BE REDUCED.
IT IS ALSO A KIND OF DEFOAMER WITH WETABILITY WHILE DISPERSING THE PIGMENTS MORE EFFIENTLY.
IT IS APPLICABLE TO PIGMENTS, INKS AND ADHESIVE.
30% OF DISPERSING AGENT USAGE AMOUNT
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
SUBSTRATE WETTING AGENT WITH DEFOAMING CAPACITY |
100 |
HYPERBRANCHED POLYETHER |
NONE |
SPECIFIC GRAVITY: 0.98-1.03 |
PH 5-8 |
THE PRODUCT IS USED IN WATER-BASED SERIES OF INDUSTRIAL PAINTS WITH DEFOAMING FUNCTION, BETTER GLOSS AND GOOD WETTABILITY AND WITHOUT SILICON, APEO AND SOLVENT.
IT HAS GOOD WETTABILITY FOR SUBSTRATE OF METAL, TIMBER AND PLASTICS.
THERE IS NO INFLUENCE ON REPAINTING BECAUSE OF ITS HIGH SALT SPRAY RESISTANCE IN ANTICORROSIVE PIGMENTS.
IT IS NOT FOAM STABILIZER. WETTABILITY CAN BE ACHIEVED WHEN IT IS USED AS DEFOAMER.
0.25%-0.75% OF THE TOTAL QUANTITY OF THE FORMULA.
IT CAN BE USED IN ANY PRODUCTION PHASES.
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
MULTIFUNCTIONAL NEUTRALIZER |
95 |
MIXTURE OF SPECIAL ALCAMINES |
PROPYLENE GLYCOL |
SPECIFIC GRAVITY: 0.98-1.03 |
ODORLESS |
IT IS ALKALINE.
THE PROCESS OF EPOXY CURING CAN BE PROMOTED WITH IT.
pH VALUE OF IT IS STABLE.
DISPERSIBILITY OF THE DISPERSING AGENT CAN BE IMPROVED WITH IT.
WATER RESISTANCE AND SALT SPRAY RESISTANCE CAN BE IMPROVED WITH IT.
IT IS APPLICABLE TO INDUSTRIAL WATER-BASED COATINGS.
IT CAN BE USED IN THE FIELD WITH STRICT REQUEST FOR VOC WITH ITS HIGH VOLATILITY, EG. FURNITURE COATINGSS, INTERIOR WALL COATINGSS.
0.05%-0.2% OF TOTAL QUANTITY OF THE SYSTEM
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
MULTIFUNCTIONAL NEUTRALIZER |
95 |
MIXTURE OF SPECIAL ALCAMINES |
DPM |
VALUE OF VAPOUR PRESSURE: mmHg/pa(20℃)0.08/10.6 |
NEUTRALIZATION EQUIVALENT: 92-98 |
IT IS ALKALINE.
THE PROCESS OF EPOXY CURING CAN BE PROMOTED WITH IT.
pH VALUE OF IT IS STABLE.
DISPERSIBILITY OF THE DISPERSING AGENT CAN BE IMPROVED WITH IT.
WATER RESISTANCE AND SALT SPRAY RESISTANCE CAN BE IMPROVED WITH IT.
IT IS APPLICABLE TO WATER-BASED INDUSTRIAL COATINGS.
0.05%-0.2% OF TOTAL QUANTITY OF THE SYSTEM
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
ADHESION PROMOTER |
85 |
WATER-SOLUBLE EPOXY SILANE |
WATER |
REFRACTIVE INDEX: 1.3895 |
TRANSPARENT |
IT IS EPOXY SILANE OLIGOMER WITH GOOD EPOXY REACTIVITY AND BETTER STORAGE STABILITY.
MECHANICAL PROPERTY OF THE COMPOSITE MATERIAL CAN BE IMPROVED WITH IT.
THE COMPATIBILITY BETWEEN INORGANIC FILLER AND POLYMER CAN BE IMPROVED WITH IT.
0.5-3% OF THE FORMULA QUANTITY
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
ADHESION PROMOTER |
100 |
OLIGOMER OF EPOXY SILANE |
NONE |
FLASH POINT: 115℃ |
TRANSPARENT |
IT IS MODIFIED EPOXY SILANE OLIGOMER WHICH HAS BOTH GOOD PERFORMANCE OF WATER RESISTANCE AND WATER SPRAY RESISTANCE AS THE ADDITIVE AND PRIMER FOR COATINGS AND PAINTS.
AS THE ADDITIVE FOR ANTICORROSIVE COATINGS, IT HELPS TO IMPROVE THE DRY AND WET COHESIVE FORCE OF BASE MATERIAL SUCH AS GLASS AND METAL SIGNIFICANTLY.
IT IS FEATURED WITH CORROSIVE RESISTANCE AND IMPACT RESISTANCE.
IT TAKES ON TRANSPARENT AFTER THE TREATMENT.
0.5-2% OF THE TOTAL QUANTITY OF THE RESIN
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
ADHESION PROMOTER |
100 |
OLIGOMER OF EPOXY SILANE |
NONE |
FLASH POINT: 115℃ |
TRANSPARENT |
IT IS MODIFIED EPOXY SILANE OLIGOMER WHICH HAS BOTH GOOD PERFORMANCE OF WATER RESISTANCE AND WATER SPRAY RESISTANCE AS THE ADDITIVE AND PRIMER FOR COATINGS AND PAINTS.
AS THE ADDITIVE FOR ANTICORROSIVE COATINGS, IT HELPS TO IMPROVE THE DRY AND WET COHESIVE FORCE OF BASE MATERIAL SUCH AS GLASS AND METAL SIGNIFICANTLY.
IT IS FEATURED WITH CORROSIVE RESISTANCE AND IMPACT RESISTANCE.
IT TAKES ON TRANSPARENT AFTER THE TREATMENT.
0.5-2% OF THE TOTAL QUANTITY OF THE RESIN
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
ORGANIC SILICON DEFOAMER |
100 |
GEMINI POLYETHER -MODIFIED SILICONE OIL |
NONE |
VISCOSITY: |
WITHOUT SHRINKAGE CAVITY |
THE PRODUCT IS GOOD FOR REMOVING THE TINY BUBBLES IN THE INDUSTRIAL COATINGS.
IT IS VERY APPLICABLE TO AIRLESS AND MIXED AIR SPRAY.
HIGH VISCOSITY FORMULA IS RECOMMENDED AS IT IS USEFUL FOR EPOXY SYSTEM, ACRYLIC ACID, POLYURETHANE SYSTEM.
IT ALSO HAS THE FUCTION OF LEVELING, THUS SHRINKAGE CAVITY WILL NOT APPEAR WHILE USING THE COATINGS.
0.7% OF THE QUANTITY OF TOTAL PIGMENT FORMULA
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
ORGANIC SILICON DEFOAMER |
100 |
POLYETHER -MODIFIED SILICONE OIL MIXTURE |
NONE |
WHITE TRANSLUCENT LIQUID |
HIGH EFFICIENCY OF DEFOAMING |
THE PRODUCT IS APPLICABLE TO ALL KINDS OF WATER-BASED COATINGS.
IT HELPS TO REMOVE THE TINY BUBBLES IN THE HIGH VISCOSITY SYSTEM AND SYSTEM WITH FOAM HARD TO REMOVE.
DISPERSED DIRECTLY AND RAPIDLY, IT IS SUITABLE FOR ACRYLIC ACID, POLYURETHANE, EPOXY SYSTEM.
0.5% OF THE QUANTITY OF TOTAL PIGMENT FORMULA
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
WETTING AND LEVELING AGENT |
100 |
GEMINI SILOXANE STRUCTURE |
NONE |
VISCOSITY: |
SHRINKAGE CAVITY RESISITANT |
THE PRODUCT IS APPLICABLE TO VARIOUS WATER-BASED COATINGS WITH GOOD UNIVERSATILITY, COMPATIBILITY, LEVELING EFFECT AND SHRINKAGE CAVITYRESISTANCE.
IT IS SUITABLE FOR REDUCING THE SHRINKAGE CAVITYIN IN THE COATINGS PRODUCED BY DEFOAMER WITH LITTLE AMOUNT AND OBVIOUS EFFECT.
0.2% OF THE QUANTITY OF TOTAL PIGMENT FORMULA
TYPES |
ACTIVE INGREDIENT(%) |
CHEMICAL COMPOSITOIN |
SOLVENT |
REFERENCE DATA |
REMARKS |
MINERAL OIL DEFOAMER |
100 |
MINERAL OIL EMULSIFIED MIXTURE |
NONE |
DENSITY: 1.03g/cm |
MILK WHITE |
IT SHOWS GOOD WETTABILITY.
IT REMOVES THE TINY BUBBLES RAPIDLY WITH NO DELAMINATION, WHICH IS FASTER THAN THE GENERAL DEFOAMER DOES.
IT IS APPLICABLE TO ACRYLIC SYSTEM AND EPOXY SYSTEM.
0.03-0.2% OF THE QUANTITY OF THE MANUFACTURED COATINGS